CHN
|
属性 |
方法 |
单位 |
HI-1410G1 (PA66+C/F10%+GF10%) |
HI-1420 (PA66+C/F20%) |
HI-1430 (PA66+C/F30%) |
HI-1425M (PA66+G/F25%+MF23%) |
HI-1340 (PA6+C/F40%) |
HI-1360G (PA6+G/F60%) |
|---|---|---|---|---|---|---|---|---|
|
物理 |
||||||||
比重 |
ASTM D 792 |
g/㎤ |
1.32 |
1.22 |
1.30 |
1.48 |
1.32 |
1.70 |
成型收缩率 |
ASTM D 955 |
% |
0.1 ~ 0.5 |
0.1 ~ 0.4 |
0.1 ~ 0.4 |
0.1 ~ 0.4 |
0.1 ~ 0.2 |
0.1 ~ 0.2 |
|
机械 |
||||||||
拉伸强度 (50mm/min) |
ASTM D 638 |
kgf/㎠ |
1,500 |
2,250 |
1,900 |
790 |
2,380 |
2,050 |
弯曲强度(5mm/min) |
ASTM D 790 |
kgf/㎠ |
2,500 |
2,500 |
2,500 |
2,500 |
2,500 |
1,900 |
弯曲模量 (5mm/min) |
ASTM D 790 |
kgf/㎠ |
110,000 |
121,000 |
170,000 |
58,000 |
215,000 |
166,000 |
Izod冲击 (缺口 @ 23℃) |
ASTM D 256 |
kgf-㎝/㎝ |
13.1 |
12.5 |
10.0 |
5.0 |
12.5 |
13.3 |
|
热学 |
||||||||
热变形温度 (1.8 MPa) |
ASTM D 648 |
℃ |
245 |
252 |
250 |
186 |
210 |
213 |
|
电学 |
||||||||
表面电阻率 |
ASTM D257 |
Ohm/sq |
10⁴~10⁶ |
10²~10⁴ |
10³~10⁴ |
- |
10⁰~10³ |
- |